Covestro Bayhydur XP 2655 Hydrophilic HDI polyisocyanate Low viscosity and easy to disperse – Amine Catalysts https://www.newtopchem.com The Leading Supplier of China Amine Catalysts Wed, 01 Nov 2023 09:22:05 +0000 zh-Hans hourly 1 https://wordpress.org/?v=6.1.7 https://www.newtopchem.com/wp-content/uploads/2023/12/1.jpg Covestro Bayhydur XP 2655 Hydrophilic HDI polyisocyanate Low viscosity and easy to disperse – Amine Catalysts https://www.newtopchem.com 32 32 Covestro Bayhydur XP 2655 Hydrophilic HDI polyisocyanate Low viscosity and easy to disperse https://www.newtopchem.com/archives/43687 Wed, 01 Nov 2023 09:22:05 +0000 https://www.newtopchem.com/?p=43687 Type Hydrophilic aliphatic polyisocyanate based on hexamethylene diisocyanate (HDI), used as curing agent component of waterborne two-component polyurethane systems

Supply Form 100 %

Specifications

Features Value unit Test method
NCO content 20.3 – 21.3 % M105 -ISO 11909
Viscosity,23°C 3,500 ± 1,000 mPa ·s M014 -ISO 3219/A.3
Hazencolor value < 60   <span style=”font-famiary Water-based systems need to have the characteristics of good combination stability and chemical resistance. Although relatively weakly hydrophilic, this curing agent emulsifies easily in aqueous phases, even under the low shear forces common in commercial applications. Coatings prepared using this product form high gloss, low haze films.
Generally, when mixing with a hydrophilic curing agent, especially an ionic hydrophilic polyol dispersion, it can be diluted with water in advance or a small amount of organic co-solvent can be added to control the increase in viscosity. Due to the balance between moderate hydrophilicity and high functionality, waterborne two-component polyurethane coatings prepared with Bayhydur XP 2655 are characterized by fast drying and rapid hardening, forming films with high final hardness and excellent chemical resistance characteristics. Bayhydur XP 2655 can also be used as a crosslinking aid for waterborne polyols (Bayhydrol®) and for most neutral waterborne polymer dispersions such as polyurethane, polyvinyl acetate, polyacrylate and synthetic rubber dispersions. joint agent.
After adding Bayhydur XP 2655, the ready-to-use two-component coating must be used within the pot life. Pot life is influenced by polymer content and other components such as resins, thickeners, plasticizers, etc. In many dispersions, the end of the pot life (often a few hours) does not show signs of gelation.

Save
– Store in a Covestro airtight container;
– Recommended storage temperature: 0-30°C;
– Resists moisture, heat and foreign substances.

General Information :Hydrophilic isocyanates are very sensitive to moisture and react with water to form carbon dioxide and water-insoluble urea. It must therefore be stored in airtight containers. Water in all forms (humid air, solvents, wet containers) must be prevented because of the dangerous build-up of pressure caused by the production of carbon dioxide. High temperature storage will cause a slight increase in viscosity and color.

Storage Time
When the product is stored in full compliance with the requirements of the above “storage” clause and handled properly, the product meets the requirements within 6 months from the date of transportation stated on the transportation document. Specifications or characteristic values ​​described in the “Specification or characteristic values” clause above, as applicable. If the product exceeds the above-mentioned 6-month period, it does not mean that it no longer meets the set values ​​in the specifications or characteristic values. However, it is recommended that products older than 6 months from the date of shipment be tested before use to confirm that they still comply with the values ​​set in the specifications or characteristic values. The manufacturer does not make any promises for products that have been shipped more than 6 months from the date of shipment, and does not assume any responsibility and liability for non-compliance with specifications or set values ​​​​in the characteristic values.
]]>